Product Description: A high quality water reducible modified acrylic vehicle pigmented with Titanium dioxide or appropriate lead free coloured pigment.
Intended Uses:A fast drying, tough, non-yellowing interior/exterior Eggshel,Semi-Gloss and Gloss coating suitable for architectural, institutional and industrial service including moderately corrosive environments. Performs well on concrete, masonry, vinyl siding and suitably prepared and/or primed drywall, wood work, and metal. For use in Hospitals, Schools, Public buildings, Pulp and paper mills & Petro chemical plants. Provides a much tougher, more durable finish than conventional latex and alkyd finishes. Due to its exceptional adhesion, it can be used as a self prime finish on most non-porous substrates.
Gloss Level: Eggshell (60°: 10 to 35 & 85°: 30 to 45 )
Composition: Binder: 100% Acrylic
Spreading Rate (Gal): 27-36 m²/3.7L (290-390 ft²/3.7L)
Drying Time: Touch 30Mins, Handle 2Hrs, Recoat: 4 Hrs
Tools: Brush: Nylon or Polyester
Roller:10-13 mm
Spray: Tip .013-.017 in.
Application / Dilution: Ready to use / Up to 5% water if spraying
Clean-up: Water (Final rinse with Acetone)
VOC Level: <100g/L
Surface Preparation: Surfaces must be clean, dry & free from dust, grease, mildew & wax. Remove any loose & peeling paint and repair with patching compound. New Wood or Drywall: Seal bare surface with appropriate Latex, Hybrid or Alkyd primer for better uniformity. Previously Painted Areas: Glossy surfaces should be sanded to a dull finish or prime with an appropriate primer to provide good adhesion.
Size & Bases: Gallon - All bases (White,Deep,Accent,Clear)
Pail: Bases Available (White,Deep,Accent)
Extra Features: *Self prime finish on most non-porous areas *Removed tape immediately after painting *MPI #151 Approved
Product Description: A high quality water reducible modified acrylic vehicle pigmented with Titanium dioxide or appropriate lead free coloured pigment.
Intended Uses:A fast drying, tough, non-yellowing interior/exterior Eggshel,Semi-Gloss and Gloss coating suitable for architectural, institutional and industrial service including moderately corrosive environments. Performs well on concrete, masonry, vinyl siding and suitably prepared and/or primed drywall, wood work, and metal. For use in Hospitals, Schools, Public buildings, Pulp and paper mills & Petro chemical plants. Provides a much tougher, more durable finish than conventional latex and alkyd finishes. Due to its exceptional adhesion, it can be used as a self prime finish on most non-porous substrates.
Gloss Level: Semi-Gloss (60°: 37 to 53)
Composition: Binder: 100% Acrylic
Spreading Rate (Gal): 27-36 m²/3.7L (290-390 ft²/3.7L)
Drying Time: Touch 30Mins, Handle 2Hrs, Recoat: 4 Hrs
Tools: Brush: Nylon or Polyester
Roller:10-13 mm
Spray: Tip .013-.017 in.
Application / Dilution: Ready to use / Up to 5% water if spraying
Clean-up: Water (Final rinse with Acetone)
VOC Level: <150g/L
Surface Preparation: Surfaces must be clean, dry & free from dust, grease, mildew & wax. Remove any loose & peeling paint and repair with patching compound. New Wood or Drywall: Seal bare surface with appropriate Latex, Hybrid or Alkyd primer for better uniformity. Previously Painted Areas: Glossy surfaces should be sanded to a dull finish or prime with an appropriate primer to provide good adhesion.
Size & Bases: Gallon - All bases (White,Deep,Accent,Clear)
Pail: Bases Available (White,Deep,Accent)
Extra Features: *Self prime finish on most non-porous areas *Removed tape immediately after painting *MPI #153 & 163 Approved
Product Description: A high quality water reducible modified acrylic vehicle pigmented with Titanium dioxide or appropriate lead free coloured pigment.
Intended Uses:A fast drying, tough, non-yellowing interior/exterior Eggshel,Semi-Gloss and Gloss coating suitable for architectural, institutional and industrial service including moderately corrosive environments. Performs well on concrete, masonry, vinyl siding and suitably prepared and/or primed drywall, wood work, and metal. For use in Hospitals, Schools, Public buildings, Pulp and paper mills & Petro chemical plants. Provides a much tougher, more durable finish than conventional latex and alkyd finishes. Due to its exceptional adhesion, it can be used as a self prime finish on most non-porous substrates.
Gloss Level: Gloss (60°: 70 to 90 )
Composition: Binder: 100% Acrylic
Spreading Rate (Gal): 27-36 m²/3.7L (290-390 ft²/3.7L)
Drying Time: Touch 30Mins, Handle 2Hrs, Recoat: 4 Hrs
Tools: Brush: Nylon or Polyester
Roller:10-13 mm
Spray: Tip .013-.017 in.
Application / Dilution: Ready to use / Up to 5% water if spraying
Clean-up: Water (Final rinse with Acetone)
VOC Level: <150g/L
Surface Preparation: Surfaces must be clean, dry & free from dust, grease, mildew & wax. Remove any loose & peeling paint and repair with patching compound. New Wood or Drywall: Seal bare surface with appropriate Latex, Hybrid or Alkyd primer for better uniformity. Previously Painted Areas: Glossy surfaces should be sanded to a dull finish or prime with an appropriate primer to provide good adhesion.
Size & Bases: Gallon - All bases (White,Deep,Accent,Clear)
Pail: Bases Available (White,Deep,Accent)
Extra Features: *Self prime finish on most non-porous areas *DTM (Direct to Metal) *Osha Black in gallons *MPI #114 & 154 Approved